Zinc Oxide Desulfurization Adsorbent, which is applicable to desulfurization of residue cracking gases or syngas and purification of feed gases for organic synthesis processes. It is suitable for both higher (350--408℃) and lower(150--210℃) temperature use. It can convert some simpler organic sulfur while absorbing inorganic sulfur in gas stream.
Main reaction of the desulfurization process is as follows:
(1) Reaction of zinc oxide with hydrogen sulfide
H2S+ZnO=ZnS+H2O
(2) Reaction of zinc oxide with some simpler sulfur compounds in two possible ways:
a. Organic sulfur compounds, catalyzed by zinc oxide, react with hydrogen to form hydrogen sulfide:
CS2 + 4H2 = CH4 + 2H2S
C2H5SH + H2 = C2H6 + H2S
Then hydrogen sulfide is absorbed by zinc oxide
H2S+ZnO=ZnS+H2O
b. Zinc oxide reacts directly with organic sulfur compounds
COS + ZnO = ZnS + CO2
XINTAO ZnO Catalyst is an ideal desulfurization adsorbent for deep purification cases, especially those at higher temperature (350--400℃).
|
Model
|
Zinc oxide desulfurization adsorbent (ZnO Catalyst)
|
|
Color
|
White or light yellow
|
|
Shape
|
extrude
|
|
Normal size(mm)
|
Φ4×4--15
|
|
Bulk Density(kg/L)
|
1.0-1.3
|
|
Crushing strength(N/cm)
|
≥50
|
|
Loss on Attrition(%)
|
≤6
|
|
Breakthrough sulfur capacity, wt%
|
≥28(350℃)
≥15(220℃)
≥10(200℃)
|
|
Pressure, MPa
|
ambient to 4.0
|
|
Temperature ℃
|
180-400
|
|
Space velocity, h-1
|
1000-2000(gas)
|
|
Sulfur in feed gas, mg/m3
|
1-20 (≤200℃)
20-100 (≤250℃)
|
|
Sulfur in treated stream, ppm
|
max0.1
|
|
Loading
|
Loading depth: Higher L/D (min3) is recommended. Configuration of two reactors in series can improve utilization efficiency of the adsorbent.
Loading procedure:
(1)Clean the reactor before loading;
(2)Put two stainless grids with smaller mesh size than the adsorbent;
(3)Load a 100mm layer of Φ10—20mm refractory spheres upon the stainless grids;
(4)Screen the adsorbent to remove dust;
(5)Use special tool to ensure evenly distribution of the adsorbent in the bed;
(6)Inspect uniformity of the bed during loading. When inside-reactor operation is needed, A wood plate should be put on the adsorbent for the operator to stand upon.
(7)Install A stainless grid with small mesh size than the adsorbent and a 100mm layer of Φ20—30mm refractory spheres at the top of the adsorbent bed so as to prevent entrainment of the adsorbent and ensure even distribution of the gas stream.
Note: Evenly distribution of the adsorbent is essential to its efficient operation, which should be paid close attention to.
|
|
Start-up
|
(1)Replace the system by nitrogen or other inert gases until oxygen concentration in the gas is less than 0.5%;
(2)Preheat the feed stream with nitrogen or feed gas under ambient or elevated pressure;
(3)Heating speed: 50℃/h from room temperature to 150℃ (with nitrogen) ; 150℃ for 2 h (when heating medium is shifted to feed gas ), 30℃/h over 150℃ until required temperature is attained.
(4)Adjust the pressure steadily until the operation pressure is attained.
(5)After pre-heating and pressure elevation, the system should first be operated at half load for 8h. Then raise the load steadily when operation becomes stable till full-scale operation.
|
|
Shut-down
|
(1)Emergent shut-down
Cut feed gas (oil) supply. Close inlet and outlet valves. Keep the temperature and pressure. If necessary ,use nitrogen or hydrogen-nitrogen gas to maintain the pressure to prevent negative pressure.
(2 ) Change-over of desulfurization adsorbent
Close inlet and outlet valves. Steadily lower the temperature and pressure to ambient condition. Then isolate the desulfurization reactor from the production system. Replace the reactor with air until oxygen concentration of >20% is attained. Open the reactor and unload the adsorbent.
(3) Equipment maintenance (overhaul)
Observe the same procedure as shown above except that pressure should be lowered at 0.5MPa/10min and temperature lowered naturally.
The unloaded adsorbent shall be stored in separate layers. Analyze the samples taken from each layer to determine status and service life of the adsorbent.
|
|
Transportation and storage
|
(1)The adsorbent product is packed in plastic super sacks or iron barrels with plastic lining to prevent moisture and chemical contamination.
(2)The adsorbent product should be prevented from contact with chemicals during transportation and storage.
(3)The product can be stored for 3-5 years without deterioration of its properties if appropriately sealed.
|
Most of our customers agreed that the product is important in electronic products. It helps prevent the premature failure of the electronic components. This product has the advantage of excellent acid resistance.
People will find it easy to rinse or dishwasher safe, which saves the host much effort in cleaning during dining or gathering parties. This product has the advantage of excellent acid resistance.
Jiangxi Xintao Technology Co., Ltd. was established in the year 2002. Jiangxi Xintao Technology Co., Ltd. is a trusted name in the field of chemical industry. We are a major Manufacturer, Exporter and Supplier of Honeycomb Ceramic. Our products are recognized for their superior quality and performance. We provide activated alumina in a variety of packaging solutions to cater to the demands of clients. Our motto is to set up high standards for ourselves through our sheer hard work and dedication. The company is located in jiangxi/pingxiang/anyuan/. It runs under the ownership of . Under the esteemed guidance of our owner, we have been able to accomplish a lot in the market. Our clients have been a strong support for us in attaining this distinguished position. For achieving optimum client satisfaction, we provide trade transparent polices that are customer friendly.